Abstract
The paper presents the results of experimental researches on the formation of barium hexaferrite type M (BHFM) by microwave heating. The microwave heating process takes only a few minutes to obtain calcined barium ferrite powders. Micronic and nanometric powders of BaCO3 and α-Fe2O3 were used as raw materials. In order to obtain BHFM, the microwave heating process was used with following mixtures: stoichiometric homogeneous mixture of BaCO3 and α-Fe2O3 powders, mechanically alloyed mixtures of BaCO3 and α-Fe2O3 powders for 5 and 20 hours in wet medium using a high energy ball mill Pulverisette 4. Using high energy ball milling, the powder size was turned into nanoscale. After using the microwave heating process it was observed a significant reduction of temperature-time parameters to BHFM formation for mechanically alloyed mixtures compared to homogeneous mixture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.