Abstract
Composite coatings based on chromium carbide (Cr3C2) and nickel–chromium alloys (NiCr) are widely used due to their unique properties, including high heat resistance, wear resistance and corrosion resistance. This article studies the structural–phase and physical–mechanical characteristics of Cr3C2-NiCr composite coatings applied by high-velocity oxygen fuel to E110 zirconium alloy. The HVOF method was chosen to create coatings with high adhesion to the substrate and excellent performance properties. Analysis of the microstructure of the cross-section showed the thickness of the modified surface layer from 75 to 110 μm, depending on the processing modes. Energy dispersive X-ray spectral analysis revealed the presence of elements Cr, Ni, C and O in the coating composition. Structural–phase analysis confirmed the formation of coatings with a high concentration of Cr3C2 carbide particles and NiCr (nickel–chromium) phases. The resulting composite coatings based on Cr3C2-NiCr had a significantly high microhardness, ranging from HV 1190 to HV 1280, and the friction coefficient varied in a significant range from 0.679 to 0.502 depending on the processing conditions. The maximum adhesion strength was 9.19 MPa per square centimeter.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.