Abstract
The character of structure and the micro-area elements of inner oxidation film were investigated by using metallographic microscope, electron microscopy, energy spectrum analysis and other testing methods based on samples of superheater and reheater tube cutting from three units. The results showed that the inner wall oxide layer of T91 steel superheater tube after running exhibited a double-layer structure, including inner and outer layer, and the interface between the two layers is the original metal surface. There exists a transition zone between the inner oxide film and metal matrix. A concentration gradient of alloy element in transition zone can be observed and the intergranular oxidation is present. The Fe-rich outer oxide layer does not contain Cr, which consists of Fe3O4, and the internal oxidation layer is composed of (Fe,Cr)3O4.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.