Abstract
Gel casting is an advanced wet-forming method for ceramics. In this paper, Isoabm 104 is selected as the dispersant and gelation agent for gel casting. The optimization of gel casting slurry and the preparation of the green and sintered alumina bodies are investigated. TAC reduces the viscosity of the slurry significantly due to electrostatic interaction. Isopropanol alcohol and vacuum tank eliminates the slurry’s air bubbles, thus improving the density of green bodies. A staged drying process is necessary to produce smooth and defect-free green bodies. After optimization of the slurry formulation and gel casting process, alumina ceramics with a Weibull modulus of 11.1 are successfully prepared.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.