Abstract
In allusion to facility corrosion problem in caustic soda industry five types of ni-Cr-cu alloy cast irons were developed. The corrosion rates of ni-Cr-cu alloy cast irons in hot concentrated alkali solution were measured by using self-made dynamic corrosion experiment equipment; the microstructures and surface corrosion morphology of alloy cast irons were observed by means of the optical microscope and SEM; the composition was analyzed using XES. Corrosion resistance mechanism were discussed detailedly. the experimental results showed that ni-Cr-cu cast iron was uniform corrosion macroscopically in the dense caustic soda at high temperature and there was ni, cu enrichment microcosmically. The Ni and Cu enriched in the matrix , which increase in local electrode voltage of the matrix,are advantageous to the improvement of caustic corrosion resistances of that zone. The higher Ni content,the better alkali corrosion resistance performance with high temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.