Abstract
The Fe-Si-Al soft magnetic composites were produced by cold pressing of water-atomized Fe-Si-Al powder using organic binder. The effect of shaping pressure, annealing temperature, magnetic annealing and dielectric content on properties of Fe-Si-Al soft magnetic composites was investigated. The results showed that increasing shaping pressure increases density and radial crushing strength of Fe-Si-Al soft magnetic cores, and decreases coercivity and total loss. Increasing annealing temperature can increase effective permeability and decrease total loss owing to decreasing hysteresis loss, and over-annealing (＞660°C) can deteriorate magnetic properties. The magnetic annealing can decrease total loss of Fe-Si-Al magnetic powder core. Increasing dielectric content can reduce the eddy current loss of Fe-Si-Al magnetic powder core and decrease the real part of permeability. Fe-Si-Al magnetic powder core with shaping pressure of 1800 MPa, annealing temperature of 660 °C and dielelctric content of 0.7% presented the optimum magnetic properties with an effective permeability of 127, a total loss of 78mW/cm3 and a radial crushing strength of 18MPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.