Abstract
Silca and its composite powders added different amount of microsilica were ground in a planetary ball mill (QM-3SP4) at various grinding period with addition of a certain number of grinding aid. The effects of mechano-chemical on particle size, crystal size and lattice deformation in grinding process were analyzed. The phase compositions and size compositions of the treated powders were investigated by X-ray Diffraction (XRD) and Laser Particle Size Analyzers. With the increase of grinding time, the particle size decrease, the specific surface area increase, and the more amount of microsilica added, the smaller particle size the powders had after grinding. The XRD results showed that the diffraction peak intensity of powders weaken and gradually widen. The surface of the particle happened to amorphization, and occurred grain refinement and lattice distortion. Comparing with other treated powders, the change of the powders with the microsilica addition of 5% was larger. Even though the grinding time reached to 30h, the crystal transformation of SiO2has not been detected.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.