Abstract
In the present study, the hot deformation and dynamic recrystallization behaviors of an annealed FeCrCuNi2Mn2 high-entropy alloy were investigated through the hot compression tests. Flow curves were evaluated within a certain temperature range (700–1000 °C) and initial strain rate range (0.001–0.1 s−1), and the corresponding microstructures were assessed. Constitutive equations with strain-dependent material constants were established for the calculation of material constants and for modeling of flow stress behavior through the analysis of true stress-strain curves. The critical and peak stress and strain (dynamic recrystallization parameters) were extracted from the work hardening rate against stress curves. These parameters were then used to determine the recrystallized volume fraction under different conditions. The results indicated that with the increase in deformation temperature and decrease in strain rate, dynamic recrystallization parameters decreased. This trend was followed by an increase in recrystallized volume fraction and grain growth, resulting in a decrease in the hardness value of the alloy. Findings further revealed that the flow stress in the annealed alloy was higher compared with that in the as-cast alloy under the same deformation conditions. Microstructural observations and the evaluation of work hardening rate against stress curves showed the typical dynamic recrystallization characteristics as the dominant softening mechanism under different deformation conditions. The activation energy of hot deformation was determined to be 437 kJ/mol. In the present study, a power equation was established between critical stress and strain and the Zener–Hollomon parameter with the exponents of 0.089 and 0.086, respectively. Moreover, the dynamic recrystallization grain size was found to be proportionate to Z−0.11.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.