Abstract
Fine martensite could be gained in 70Mn2Mo cast steel roller after solidification by laser treatment. The hardness and depth of hardened zone reached 920 HV (about 65HRC) and 0.6mm respectively. After tempered in high temperature, the depth of hardened zone whose hardness was maintained above 430HV was 0.4mm. These results showed the better anti-tempering property and the higher hardness and hardened depth compared with water quenching and implied the greater applied potentiality of laser strengthening.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.