Abstract
Tensile tests and a cold deep drawing process were developed at room temperature to estimate the stamping formability of AZ31B magnesium alloy sheet. The results show that AZ31B magnesium alloy sheet has poor formability at room temperature with the total elongation of ~ 20%, the yield ratio is about 0.6 and the strain-hardening exponent is 0.18, while the plastic strain ratio is 1.58, and the earing ratio is-0.55.Thus, AZ31B magnesium alloy sheet can not suffer server plastic deformation. It was found that comparatively shallow magnesium alloy cups were satisfactorily formed at room temperature without heating when the punch fillet radius 6mm and the die fillet radius10mm with a 1mm thickness sheet with limit drawing ratio of 1.25.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.