Abstract
For widespread application, the performance of thermoset resin-benzoxazine must be progressively enhanced. A new fluoropyridine-based benzoxazine (BF-a) with high thermal stability, excellent flame-retardant performance, and a large water contact angle was synthesized using fluoropyridine, aniline, and paraformaldehyde. The chemical structure of the monomer, curing behavior, thermal stability, and flame retardancy were examined carefully. The results indicate that the curing temperature of newly synthesized benzoxazine is 227.9 °C, which is lower than that of benzoxazine derived from bisphenol A. In addition, the thermal stability and flame resistance of poly(BF-a), as measured by 5 % and 10 % weight loss temperatures (Td5 and Td10), char yield at 800 °C (Yc), limiting oxygen index (LOI), peak heat release rate (PHRR), and total heat released (THR), are at 271 ℃, 371 ℃, 69.4 %, 44.2, 7.4 J·(g K)−1 and 3.5 kJ g−1, respectively, which shows its excellent thermal properties and potential as a flame-retardant material. Furthermore, the performances of poly(BF-a) coatings are also demonstrated. Coatings based on poly(BF-a) have a water contact angle, hardness, surface adhesion, interaction energy, and corrosion rate of 123.5°, 6H, 5B, −842.83 kcal·mol−1, and 0.77 mm year−1, respectively, indicating its potential applicability in coatings for harsh environments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.