Abstract
AbstractThe corrosion resistance of MoNb/AlNd/MoNb film during different sputter conditions was studied for G6 rotating target sputter equipment. The results show that with the increase of sputter power and the increase of the thickness, top MoNb tends to form coarse columnar crystals, and the corrosion resistance of the metal thin films, at first, increases and then decreases with the increase of sputter power and metal thickness. As the sputter temperature increases, top MoNb tends to form coarse grains while the corrosion resistance of the film is poor. The result also release that with the increase of the target speed, top MoNb film becomes loose so that it is difficult to play a protective role because of its poor corrosion resistance ability. Under the same conditions, the sputter of the planar target film is denser; as a result, the top MoNb layer can protect the inner AlNd layer from corrosion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.