Abstract
Activated carbon was fabricated by using phenolic resin as carbon source, PEG as organic template, KOH as activator. The samples were analyzed by N2 adsorption, scanning electron microscopy (SEM). Cyclic voltammetry and galvanostatic charge-discharge were used to characterize the electrochemical performance of the samples. The results showed that the specific surface area of the prepared sample (AC1) was 2469 m2/g, the pore size was mainly in the range of 1.0～4.0 nm. At a current density of 7.5 mA/cm2, a specific capacitance of 327F/g was achieved, the equivalent series resistance (ESR) was 0.8Ω. Supercapacitors based on the sample have low ESR and excellent power property. For comparison, commercial AC (AC2) was also studied.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.