Research and Preparation of Silver Free Amorphous Active Brazing Alloy

Abstract

A silver free amorphous Cu-35Ti-12Ni active brazing alloy was successfully prepared in this work. The crystallinity, microstructure, and chemical composition were characterized with X-ray diffraction (XRD), scanning electron microscope (SEM), and energy-dispersive spectrometry (EDS), respectively. A typical characteristic peak of amorphous material was observed in the XRD pattern. The microstructures and chemical compositions of the silver free amorphous alloy were uniform. Differential scanning calorimetry (DSC) result shows that the amorphous silver free brazing alloy has higher melting temperature than commercial silver brazing alloy (Ag-26.5Cu-1.5Ti). Wetting contact angle and spreading area on Si3N4 ceramic substrate were used to evaluate the wetting ability of brazing alloy. The wetting angle was smaller than 5o, and the spreading area was 141.6 mm2 at 1100°C. The bending strength of silver free brazing alloy/Si3N4 was also carried out. The mechanical test shows that the amorphous Cu-35Ti-12Ni/Si3N4 has higher joint strength (304.7MPa) than the crystal Cu-35Ti-12Ni/Si3N4 (294.7MPa) at room temperature.