Abstract

At the inner baffle of the AUG divertor massive polished inserts of tungsten and P92 steel were installed to measure the erosion by arcing. For tungsten most of the traces are less than 0.4µm deep and a similar amount of tungsten is deposited close to the traces. Few craters up to 4µm resulting in an average erosion rate of 2×1013 at cm−2s−1 are observed. The behaviour for P92 steel is quite different: most of the traces are 4µm deep, up to 80µm were observed. An average erosion rate of 400×1013 at cm−2s−1, i.e. more than a factor of hundred higher compared to tungsten, is found. Therefore, erosion by arcing has to be taken into account to determine the optimal material mix for future fusion devices.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.