Replacement of Ni by Mn in High-Ni-Containing Austenitic Cast Steels used for Turbo-Charger Application

Abstract

High-temperature tensile properties of austenitic cast steels fabricated by replacing Ni by Mn in a 20 wt pct Ni-containing steel were investigated. In a steel where 8 wt pct Ni was replaced by 9.2 wt pct of Mn, 17.4 and 9.8 pct of ferrite existed in equilibrium phase diagrams and actual microstructures, respectively, because a role of Mn as an austenite stabilizer decreased, and led to deterioration of high-temperature properties. When 2 to 6 wt pct Ni was replaced by 2.3 to 6.9 wt pct Mn, high-temperature properties were comparable to those of the 20 wt pct Ni-containing steel because ferrites were absent, which indicated the successful replacement of 6 wt pct Ni by Mn, with cost reduction of 27 pct.