Removal of vanadium from industrial wastewater using iron sorbents in batch and continuous flow pilot systems

Abstract

This study investigated the removal of vanadium from real industrial wastewater by using six iron materials: commercial iron sorbent (CFH-12), commercial mineral sorbent (AQM), blast furnace sludge (BFS), steel converter sludge (SCS), ferrochrome slag (FeCr) and slag from a steel foundry (OKTO). Batch tests revealed that CFH-12 (ferric oxyhydroxide) removed vanadium most efficiently, which was explained by its high iron content and the amorphous form of the iron, and that the sorption followed the Langmuir isotherm. With a dosage of 10 g/l and an initial vanadium concentration of 58.2 mg/l, 91–94% removal rates for vanadium were achieved in the studied pH range (3–9). Other sorbents showed significantly lower efficiency than CFH-12, with the exception of BFS at acidic pH (93%). Based on the batch test results, CFH-12 was selected for a pilot study made on site. The pilot study demonstrated the feasibility of CFH-12 to remove vanadium at high temperature (80 °C) from concentrated industrial wastewater with fluctuating water quality (vanadium concentration varied from 51 to 83 mg/l, pH about 9 (at 25 °C)). Leaching of impurities (mainly S, Ca, Mg and K) into the effluent occurred during the first day, but subsequently good quality effluent was produced (e.g. <0.1 mg/l V). During the pilot study, the amorphous iron material of CFH-12 was crystallized into a hematite-like phase (Fe1.67 H0.99 O3), and goethite (FeO(OH)) with a higher average pore diameter, probably due to the hot process conditions to which CFH-12 was exposed for over five days.