Abstract
The objectives of this study were to determine the viability of removing Orange II (OII) dye by simulated solar photoelectro-Fenton (SSPEF) and to evaluate the stability of a WO2.72/Vulcan XC72 gas diffusion electrode (GDE) and thus determine its best operating parameters. The GDE cathode was combined with a BDD anode for decolorization and mineralization of 350 mL of 0.26 mM OII by anodic oxidation with electrogenerated H2O2 (AO-H2O2), electro-Fenton (EF) and photoelectro-Fenton (PEF) at 100, 150 and 200 mA cm−2 and SSPEF at 150 mA cm−2. The GDE showed successful operation for electrogeneration, good reproducibility and low leaching of W. Decolorization and OII decay were directly proportional to the current density (j). AO-H2O2 had a reduced performance that was only half of the SSPEF, PEF and EF treatments. The mineralization efficiency was in the following order: AO-H2O2 < EF < PEF ≈ SSPEF. This showed that the GDE, BDD anode and light radiation combination was advantageous and indicated that the SSPEF process is promising with both a lower cost than using UV lamps and simulating solar photoelectro-Fenton process. The PEF process with the lowest j (100 mA cm−2) showed the best performance-mineralization current efficiency.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.