Abstract
Ag-Cu-Ti/Cu/Ag-Cu-Ti composite interlayer was successfully designed to braze Al2O3 ceramic and Nb. The effect of the addition of Cu interlayer with various thicknesses on the microstructure, residual stress and mechanical properties of the brazed joints was investigated by finite element modeling (FEM) computation combined with experimental verification. The results showed that the layered Ag-Cu-Ag solid solution structure formed in the Al2O3/Nb brazed joints when the composite interlayer was used. Moreover, the thickness of TiO + Ti3Cu3O reaction layers adjacent to the Al2O3 ceramic substrate did not change obviously regardless of the Cu foil thickness. The maximum residual stress in the whole brazed joint always appeared in the Al2O3 ceramic substrate nearby the interlayer, but it was reduced from 384 MPa to 119 MPa when a 150 μm thick Cu foil was added. The variation of calculated residual stresses as a function of Cu foil thickness, which was verified by X-ray measurement, exhibited a consistent with Al2O3 ceramic strain energy. Thus, the calculation of Al2O3 ceramic strain energy could be a good criterion to evaluate the joint shear strength because the fracture occurred in the Al2O3 ceramic. The reduction of detrimental residual stress was primarily attributed to the increased plastic strain energy of Cu interlayer. The FEM and experiment results indicated that the ability of plastic deformation of the interlayer played a key role in determining the residual stress in the brazed joint, providing a method for improving the bonding properties of ceramic and metal.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.