Abstract
PurposeThe purpose of this paper is to evaluate the lead‐free solder joint reliability of a variety of surface mount components assembled onto printed circuit boards (PCBs) under a number of different tests.Design/methodology/approachLead‐free solder with a composition of Sn96.5‐Ag3.0‐Cu0.5 was used in a surface mount reflow process. Different types of surface mount dummy components with a daisy chain, such as CBGAs, BGAs, PLCCs, CSPs, and QFNs, were assembled onto PCBs. Both the mechanical and thermo‐mechanical reliability of the solder joints were evaluated by several tests. The experiments included package shear, package pull, three‐point bending and accelerated thermal cycling testing for 2,000 cycles. The packages were examined by X‐ray and C‐SAM before the reliability tests were carried out. The maximum load and the corresponding load‐displacement curve were recorded in the mechanical test.FindingsThe results from the mechanical tests show the major failure mode is on the copper pad. Weibull analysis shows that the characteristic lives of most packages are between 1,100 and 2,400 cycles. For the CBGA, the characteristic life of 96 cycles is relatively short, due to the serious CTE mismatch. Cross‐section inspection shows failures occur at the solder joint. Copper pad failure is also observed.Originality/valueThis paper provides both the mechanical and thermal‐mechanical reliability of lead‐free solder joints. The experimental data are very useful in the lead‐free SMT industries.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.