Abstract
ABSTRACTWe fabricated ferroelectric (Pb,La)(Zr,Ti)O3 (PLZT) capacitors with Sn:In2O3 (ITO) or Pt top electrodes and investigated the ferroelectric properties of these PLZT capacitors. The shape of polarization–voltage hysteresis loops was essentially unchanged and the decrease in the remnant polarization of the ITO/PLZT/Pt capacitors was smaller than that of the Pt/PLZT/Pt capacitors after annealing with 3% D2 (in N2) at 200°C and 1 Torr (i.e., FGAD). Time of flight secondary mass spectrometry revealed that the D atoms were incorporated into the PLZT film of the Pt/PLZT/Pt capacitors after 3% D2 annealing, resulting in a decrease in the ferroelectric properties. In comparison, no D ion signal was detected in the PLZT film after FGAD for ITO/PLZT/Pt capacitors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.