Abstract
The interfacial reactions and shear properties of Sn-37Pb (wt.%) solder bumps with two different under bump metallizations (UBMs), Cu and Ni, were investigated after high temperature storage (HTS) tests at 150 C for up to 65 days. Two different intermetallic compounds (IMCs), Cu6Sn5 and Cu3Sn, were formed at the bump/Cu interface, whereas only a Ni3Sn4 IMC layer was formed at the bump/Ni interface. The thicknesses of these IMCs increased linearly with the square root of duration time. The IMC growth rate at the bump/Cu UBM interface was much greater than that at the bump/Ni UBM interface. The shear properties of the bumps with the Cu UBM were greatly decreased with increasing duration time, compared with those with the Ni UBM.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.