Abstract
The ferroelectric properties of 500Å thick strained, epitaxial SrTiO3 films grown on DyScO3 substrates by reactive molecular-beam epitaxy are reported. Despite the near 1% biaxial tensile strain, the x-ray rocking curve full widths at half maximum in ω are as narrow as 7arcsec (0.002°). The films show a frequency-dependent permittivity maximum near 250K that is well fit by the Vogel-Fulcher equation. A clear polarization hysteresis is observed below the permittivity maximum, with an in-plane remanent polarization of 10μC∕cm2 at 77K. The high Tmax is consistent with the biaxial tensile strain state, while the superimposed relaxor behavior is likely due to defects.