Abstract
AbstractThis publication highlights the structure–property relationships in several thermoplastic elastomers (TPEs): one poly(ether‐block‐amide) and two thermoplastic polyurethane elastomers with ester and ether soft blocks. Structural changes are induced by chemical degradation from virgin samples through hydrolysis and oxidation. Molar mass measurements show an exclusive chain scission mechanism for all TPEs, regardless of the chemical modification condition. Mechanical behavior was nevertheless obtained from uniaxial tensile testing and fracture testing while considering the essential work of fracture (EWF) concept. During the macromolecular scission process, elongation at break shows a plateau followed by a drop, while stress at break decreases steadily. Once again, the trend is identical for all TPEs in all conditions considered. The βwp parameter determined using the EWF concept exhibits an interesting sensitivity to scissions (i.e., molar mas decrease). Plotting elongation at break as a function of molar mass reveals a strong correlation between these two parameters. This master curve is particularly remarkable considering the range of TPEs and chemical breakdown pathways considered (hydrolysis and oxidation at several temperatures). Relevant structure–property relationships are proposed, highlighting that molar mass is a predominant parameter for determining the mechanical properties of thermoplastic elastomers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.