Abstract
In this study, the influence of oxygen diffusion on the physical properties of Ti–6Al–2Sn–4Zr–2Mo–0.1Si was examined. Measurements were carried out directly on sample cross sections which were preoxidized at high temperature. The lattice parameter evolution was measured using synchrotron X-ray diffraction and was coupled with microhardness and electron probe microanalyzer results with the aim of highlighting their relationships. The results show that the hardness and oxygen gradients along the oxygen diffusion zone in the alloy are similar to the evolution of the α-phase unit-cell volume quantified by X-ray diffraction. Linear relationships were found between these three parameters.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.