The current density in copper electroplating is directly related with the productivity; then, to increase the productivity, an increase in current density is required. This study is based on an analysis of changes in surface characteristics and mechanical properties by applying the addition of Alcian Blue (AB, C56H68Cl4CuN16S4). The amount of Alcian Blue in the electrolytes is changed from 0 to 100 ppm. When Alcian Blue is added at 20 ppm, a seed layer is formed homogeneously on the surface at the initial stage of nucleation. However, crystals electroplated in electrolytes with more than 40 ppm of Alcian Blue are observed to have growth in the vertical direction on the surface and the shapes are like pyramids. This tendency of initial nucleation formation causes protrusions when the thickness of copper foil is 12 μm. Thereafter, a lot of extrusions are observed on the group of 100 ppm Alcian Blue. Tensile strength of groups with added Alcian Blue increased by more than 140% compare to no-addition group, but elongation is reduced. These results are due to the decrease of crystal size and changes of prior crystal growth plane from (111) and (200) to (220) due to Alcian Blue.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.