Abstract
Polycrystalline samples of ScRh3Bx, which consists of reactive Sc and high melting point Rh and B elements, have been successfully synthesized by the arc melting method. ScRh3Bx has the perovskite cubic structure (space group Pm3m). Perovskite-type ScRh3Bx exists in the range of 0≤x≤1.000 (0 to 20mol%B). ScRh3 has the AuCu3 type structure (space group Pm3m). The lattice parameter a in annealed ScRh3Bx depends on x, and varies linearly from a=0.3903(1)nm (x=0) to 0.40799(3)nm (x=1.000). The micro-Vickers hardness of the annealed ScRh3Bx increases with increasing B content in the range x=0-1.000, from 1.9(±0.1)GPa for ScRh3 (0mol%B) to 9.9(±0.1)GPa for ScRh3B1.000 (20mol%B). TG analysis indicates that the onset temperature of oxidation for ScRh3B1.000 is 595°C. The sharp exothermic peak of the DTA curve is found at 797°C. Weight gain of the sample by heating in air up to 1200°C is 12.7%. The sample changed to Rh plus Sc2O3 and ScBO3 after oxidation. The weight gain of the sample decreases with decreasing boron content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.