Abstract
In order to study the relation between martensitic transformation temperature range ΔT (where ΔT is the difference between martensitic transformation start and finish temperature) and lattice distortion ratio (c/a) of martensitic transformation, a series of Ni46Mn28−xGa22Co4Cux (x = 2–5) Heusler alloys is prepared by arc melting method. The vibration sample magnetometer (VSM) experiment results show that ΔT increases when x > 4 and decreases when x < 4 with x increasing, and the minimal ΔT (about 1 K) is found at x = 4. Ambient X-ray diffraction (XRD) results show that ΔT is proportional to c/a for non-modulated Ni46Mn28−xGa22Co4Cux (x = 2–5) martensites. The relation between ΔT and c/a is in agreement with the analysis result obtained from crystal lattice mismatch model. About 1000-ppm strain is found for the sample at x = 4 when heating temperature increases from 323 K to 324 K. These properties, which allow a modulation of ΔT and temperature-induced strain during martensitic transformation, suggest Ni46Mn24Ga22Co4Cu4 can be a promising actuator and sensor.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.