Abstract
NiCu/Cu multilayers were grown on (110) textured polycrystalline Cu substrates from a single electrolyte containing Ni and Cu ions by electrodeposition. The structural, magnetic and magnetoresistance properties of the NiCu/Cu multilayers were investigated as a function of the ferromagnetic layer thickness. The ferromagnetic NiCu layer thickness of the multilayers was varied from 2 to 10 nm while the nonmagnetic Cu layer thickness was fixed at 1 nm. Energy dispersive X-ray analysis revealed that the Ni content of the films increased and Cu content decreased as the NiCu layer thickness increased. Multilayers have the face centred cubic structure with (220) preferred orientation as their substrates. Also, the highest peak intensity changed from (220) to (111) with increasing NiCu layer thickness. The saturation magnetization, Ms and the coercivity, Hc of the samples was significantly affected by the film compositions that were varied by the ferromagnetic layer thicknesses. The Ms was increased from 36 to 239 emu/cm3 and the Hc increased from 6 to 94 Oe with increasing ferromagnetic layer thickness. The multilayers exhibited either giant magnetoresistance (GMR) or the anisotropic magnetoresistance (AMR) depending on the NiCu layer thickness. The maximum GMR magnitude of 1.5 % was obtained for the films with 4 nm NiCu layer thickness. The MR measurements indicated that the films with the NiCu layer thickness up to ≤4 nm exhibited the GMR effect whereas for the films with 5 nm NiCu thickness the AMR effect appeared, and then the amount of GMR conversion to AMR effect increased as the NiCu layer thickness in the films increased from 5 to 10 nm. Thus, the variation in microstructure of the multilayers and corresponding magnetisation and magnetoresistance changes may arises from the NiCu layer thickness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.