Abstract
Abstract This investigation explores the reinforcement effects of both boron nitride nanotubes (BNNTs) and micro-boron carbide (μB4C) on the tribological and mechanical properties of aluminum matrix composite (MMC) cold-sprayed coatings. The synthesis process involved high-energy ball milling (HEBM) and cold spraying with helium to create four distinct Al-MMC coatings on a magnesium (AZ31) substrate. These coatings consisted of pure aluminum, a composition containing 4 vol% B4C, a composition with 4 vol% BNNTs, and a composition with 2 vol% B4C and 2 vol% BNNTs. Successful dispersion of nanoparticles within the aluminum matrix was achieved. The hardness of the coatings exhibited significant improvements compared to the pure aluminum coating. Specifically, the Al-BNNT coating showed a hardness increase of 14.1%, the Al-B4C-BNNT coating displayed a hardness increase of 20.8%, and the Al-B4C coating demonstrated the highest increase of 33.3% over the pure aluminum coating. Furthermore, the Al-B4C coating exhibited remarkable reductions in wear volume loss and wear track depth, amounting to eight and two orders of magnitude, respectively. Adhesion testing revealed that the Al-B4C-BNNT coating failed cohesively, while the pure aluminum coating failed adhesively at approximately the same force. The Al-B4C coating experienced a combination of the two failure modes at a 31.2% increase in force compared to the pure aluminum coating. Tensile testing stress versus strain curves indicated that the load was partially supported by the cold spray coating until the coating ruptured.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.