Abstract

This study focused on the experimental investigation of the effect of palm kernel shell particulate reinforcement on the mechanical properties of cement-based tiles. Five samples of cement tiles reinforced with different compositions of kernel shell of 1440 µm particle size at predetermined moisture content were produced against a control sample to ascertain the composition that offered the best suitable properties for the functional requirements of cement tiles at reduced cost. For all the samples produced, evaluations for bulk density, apparent porosity, water absorption capacity, and flexural strength were investigated. The results showed that porosity, water absorption capacity, and apparent density decreased with an increase in the palm kernel shell compositions while bulked density increased. The variation with 80 % cement and 20 % palm kernel shell fibre reinforcement (Sample B) demonstrated optimal tile quality with apparent porosity of 10.35 %, a water absorption capacity of 5.47 %, bulk density of 1.89 g/cm3, and flexural strength of 37.21 kgF/ cm2 . It was evident that the flexural strength of sample B met the ASTMC293 standard cement tiles requirement of 35 kgF/cm2 to 40 kgF/ cm2 thus the optimal volume fraction with improved surface characteristics and recommended for applications where hard and heavy materials are used on tiles.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call