Abstract
The effect of a deep cryogenic treatment on the microstructure of a super-bainitic steel was investigated. It was shown that quenching the super-bainitc steel in –196°C liquid nitrogen resulted in the transformation of retained austenite to two phases: ~20 nm thick martensite films and some nano carbides with a ~25 nm diameter. Some refinement of the retained austenite occurred, due to formation of fine martensite laths within the retained austenite. The evolution of these new phases resulted in an increase in the average hardness of the super-bainitic steel from 641 to ~670 HV1.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.