Abstract
Composite coatings of niobium nitride containing bismuth inclusions were deposited using a dual magnetron sputtering system with independent power suppliers for each targets; Bi and Nb. The deposition was performed under and Ar/N2 atmosphere at a 2.3 flow rate ratio, which allows the stoichiometric NbN phase to be obtained. The aim of this work was to evaluate the effect of increasing concentrations of Bi, proposed as a lubricous second phase, in the structural, mechanical and tribological properties of niobium nitride (NbN) coatings, searching for a reduction in the coefficient of friction but trying to keep hardness values larger than the tool steels (>10 GPa). The power applied to the Nb target was fixed, while the power on the Bi target was increased; obtaining Bi atomic percentage values of 1.7, 4.9 and 8.4 at%. The Bi inclusions showed different sizes and distribution in the volume and surface of the coatings. The results indicated a reduction in the hardness from 30 GPa of the NbN coating to 13.9 GPa for the highest Bi concentration. However, a more significant reduction was observed for the coefficient of friction (CoF) from 0.8 of the NbN to 0.3 for Bi concentrations between 4.9 and 8.4 at%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.