Abstract
(CdZn)Te with the composition of 3% Zn and In-doped CdTe single crystals were annealed at various annealing temperatures and under various Cd or Te pressures with the aim of eliminating Te or Cd inclusions. Te inclusions were reduced by Cd-saturated annealing at temperatures above 660°C. Only small (<1 μm) residual dark spots, located at the original position of as-grown inclusions, were observed after annealing. The size of Cd inclusions was reduced by Te-rich annealing at temperatures higher than 700°C. A specific cooling regime was used to eliminate new small Te precipitates (∼1 μm) concurrently formed on dislocations during Te-rich annealing. Poor infrared transmittance of samples with Cd inclusions was detected after Te-rich annealing; therefore, Cd-saturated re-annealing of annealed samples was used for increasing infrared transmittance to a value above 60%. Alternative models explaining the formation of star-shaped corona-surrounding inclusions are discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.