Abstract
Copper metal clusters of 4–5 A have been intercalated in the interlayers of montmorillonite by in situ reduction of bulky copper acetate hydroxide species with ethylene glycol (polyol process) at 195 °C. Various amounts of CuII as copper acetate hydroxide hydrate in excess of ion-exchange capacity were introduced into the interlayers by titrating copper acetate solution with sodium hydroxide in the presence of montmorillonite. The exchange of fully developed copper acetate hydroxide hydrate interlayers in the montmorillonite gave a basal spacing of 19.6 A. The reduced samples exhibited a basal spacing of 14.4 A indicating the presence of 4.8 A copper metal clusters after subtracting the thickness of the silicate layer (9.6 A). Further evidence for formation of copper metal clusters in the interlayers was obtained from transmission electron microscopy (TEM) and UV-VIS-NIR spectroscopy. Both water sorption isotherms and nitrogen B.E.T. surface-area measurements indicated the porous nature of Cu metal intercalated phases similar to pillared clays. During the process of reduction, large amounts of copper metal particles were expelled from the interlayers which grew to ca. 0.1-0.5 µm on the external surfaces of montmorillonite.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.