Reducing the heterogeneity of xylan through processing

Abstract

Glycerol thermal processing (GTP) of hardwood biomass at temperatures between 200 and 240°C facilitated stepwise biopolymer fractionation, while limiting significant degradation of the major hemicellulose, glucuronoxylan, into water-extractable oligosaccharides. After GTP pretreatment and sequential water and organic solvent extraction, up to 80% of the initial xylan remained in the pretreated biomass. The majority of the xylan from GTP pretreated and water/solvent extracted biomass was removed using a mild alkali extraction and the composition was compared to xylan directly isolated from untreated hardwood. The precipitated xylan from the neutralized alkaline filtrate was isolated as a water insoluble xylan portion (WIX). The residual xylan dissolved in the neutralized filtrate was precipitated in cold methanol and recovered as the water soluble xylan portion (WSX). Results showed that xylan in WIX was in a polymeric form with a number average degree of polymerization (DP) over 100, whereas the WSX had a much lower average DP of 27 (ca) and contained more substitution. As the processing severity increased during GTP pretreatment, the proportion of WIX increased and the purity of the xylan within the WIX sample reached 84% based on compositional analysis. FT-IR analysis of WIX revealed that xylan isolated after GTP contained peaks related to a reduced carbonyl signal compared to the control. Furthermore, crude WSX contained less xylan with more lignin contamination at severe GTP conditions. The recovery of the xylan in two portions facilitated a preferential purification strategy resulting in WIX with an extremely narrow polydispersity index between 1.1 and 1.25, dependent upon the GTP severity. This study provided insight into fractionating higher molecular weight xylan that may serve value-added applications such as healthcare materials and advanced packaging.