Reducibility of nickeliferous limonitic laterite ore from Central Anatolia

Abstract

Limonitic nickel laterite from Sivrihisar reserve in Turkey was reduced at 700–1100°C by the addition of 5·74, 8·61 and 11·48 wt-% coal under an argon atmosphere. The run-of-mine ore and the reduced samples were studied using X-ray diffraction. The metallisation of Fe was found to be limited up to 900°C, but increased rapidly at higher temperatures. The metallisation of Ni and Co increased when the temperature was increased from 700 to 800°C, almost levelled off up to 900°C and then increased up to 1100°C. The results also showed that increased coal additions did not affect Fe metallisation up to 900°C. At 1000°C the metallisation of Fe became slightly better, but its effect was more pronounced at 1100°C. The increased coal addition affected the nickel reduction equally at all temperatures, while it had no effect on the metallisation of Co.La réserve de nickel limnétique en Turquie a été réduit à 700-1100 ° C par l'addition de 5.74, 8.61 and 11.48 wt-% de charbon sous atmosphère d'argon. Le minerai et les échantillons réduits ont été étudiés par DRX. La métallisation de Fe a été jugée limitée à 900 ° C, mais elle a augmenté rapidement à des températures plus élevées. La métallisation de Ni et Co a augmenté lorsque la température a été augmentée de 700 à 800 ° C, presque stabilisé jusqu'à 900 ° C puis 1100 ° C. Les résultats ont également montré que l'augmentation des ajouts de charbon n'a pas affecté Fe métallisation jusqu'à 900° C. A 1000 ° C, la métallisation de Fe s'est un peu ameliorée, mais son effet était plus prononcé à 1100 ° C. L'augmentation du taux de charbon a affecté une constante réduction de nickel à toutes les températures, alors qu'il n'a eu aucun effet sur la métallisation de Co.