Red emission enhancement from CaMoO4:Eu3+ by co-doping of Bi3+ for near UV/blue LED pumped white pcLEDs: Energy transfer studies

Abstract

CaMoO4:Eu3+ (3 at. %)/Bi3+ (x at. %) nanophosphors were synthesized hydrothermally. All the samples can be excited by 280, 320, 393, and 464 nm (blue) wavelengths for generation of red color emission. Enhancement in 5D0 → 7F2 (615 nm) emission (f-f transition) of Eu3+ is observed when Bi3+ is incorporated in CaMoO4:Eu3+. This is due to the efficient energy transfer from Bi3+ to Eu3+ ions. Introduction of Bi3+ in the system does not lead to the change of emission wavelength of Eu3+. However, Bi3+ incorporation in the system induces a shift in Mo-O charge transfer band absorption from 295 to 270 nm. This may be due to the increase in electronegativity between Mo and O bond in the presence of Bi3+ leading to change in crystal field environment of Mo6+ in MoO42−. At the optimal concentration of Bi3+, an enhancement in emission by a factor of ∼10 and 4.2 in the respective excitation at 393 (7F0 → 5L6) and 464 nm (7F0 → 5D2) is observed. The energy transfer efficiency from Bi3+ to Eu3+ increases from 75% to 96%. The energy transfer is observed to occur mainly via dipole-dipole interactions. Maximum quantum yield value of 55% is observed from annealed CaMoO4:Eu3+ (3 at. %) when sensitized with Bi3+ (15 at. %) under 464 nm excitation. From Commission International de I'Eclairage chromaticity coordinates, the color (red) saturation is observed to be nearly 100%.