Abstract
This research aims to produce green cement, as an alternative to traditional cement, with outstanding performance. Five alkali-activated cement pastes were fabricated based on NaOH-activation of slag (GGBFS), bypass (B), and/or silica fume (S). Codes of five pastes are C, C-20B, C-30B, C-10B10S, and C-20B10S, as C is the control paste containing 100% slag. The compressive strength of the fabricated pastes was measured at different curing regimes: Conventional curing for 3 months and autoclave curing at 4bar/153◦C, 7bar/178◦C, and 10bar/198◦C for 4h. XRD, TGA/DTG, SEM/EDX, and BET/BJH techniques were utilized to clarify the phase development, morphological and texture features of the formed alkali-activated composite pastes. Besides, the removal capacity of some pastes for methylene blue and indigo-carmine dyes from aqueous media was evaluated. The results confirmed that C and C10B10S (80%GGBFS + 10%B + 10%S) pastes have significant mechanical properties and distinctive meso-porosity that can remove both anionic and cationic dyes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.