Abstract
Hydrogen decrepitation process has been applied for the first time for the direct recycling of SmCo5 magnets. Industrially produced sintered SmCo5 magnets were decrepitated by hydrogen gas at a pressure of 1 bar to 9.5 bar at room temperature in a planetary rotating jar. After decrepitation, the starting sintered magnets were reduced to a powder with a particle size of less than 200 µm. The produced powder was used for the preparation of recycled SmCo5 magnets. Scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction studies and magnetic measurements were used to follow the decrepitation and the sintering processes. The measured remanence and maximum energy product of the recycled magnet are 0.94 T and 171.1 kJ/m3, respectively, in comparison with 0.91 T and 156.8 kJ/m3, respectively for the original magnet before recycling. It was also observed that, there is refinement in the microstructure after recycling in comparison to the original magnet.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.