Abstract
The main objective of this paper was to investigate the alkali activation of mine tailings (MT) after mechanochemical activation and the effect of metakaolin (MK) addition. Finnish mica-rich tailings from a phosphate mine were studied as precursors for alkali-activated materials (AAM) with a potential application as a substitute for ordinary Portland cement (OPC). The principal physical properties (water absorption, apparent porosity and unconfined compressive strength) were measured for samples containing 30% to 70% tailings. Zeolite phases such as natrolite and cancrinite were observed and the formation of C-(N)-A-S-H11C-CaO, N-Na2O, A-Al2O3, S-SiO2, H-H2O. and N-A-S-H gels was identified by XRD, DRIFT, FESEM-EDS and NMR technologies. A life cycle assessment (LCA) was conducted on specimens in comparison to OPC. This work indicated that phosphate MT can be recycled through alkali activation with lower CO2 emission compared to all-metakaolin geopolymers and that the binder phase formed at the most promising tailings contents (60– 70%) was C-(N)-A-S-H gel.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.