Abstract
La[Formula: see text]Hf[Formula: see text]MnO3 films were grown on 0.05 wt.% Nb-doped SrTiO3 substrates by pulsed laser deposition. X-ray diffraction measurements demonstrated that our samples were of good epitaxy and single-crystal. The temperature-dependent resistance has been investigated. It was observed that the as-grown film of La[Formula: see text]Hf[Formula: see text]MnO3 exhibited a typical paramagnetic-ferromagnetic transition. Heterojunctions of La[Formula: see text]Hf[Formula: see text]MnO3/0.05 wt.% Nb-doped SrTiO3 exhibited-asymmetric current–voltage characteristics and a remarkable temperature-dependent rectifying behavior in a wide temperature range (from 40 K to 300 K). And the most remarkable observation of this work is the existence of a crossover from positive to negative magnetoresistance in the La[Formula: see text]Hf[Formula: see text]MnO3/0.05 wt.% Nb-doped SrTiO3 heterojunction as the temperature decreases. A temperature-dependent magnetoresistance was studied as well. The rectifying characteristics and tunable magnetoresistance of these heterojunctions may be attributed to band structure of La[Formula: see text]Hf[Formula: see text]MnO3/0.05 wt.% Nb-doped SrTiO3 heterojunction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.