Abstract
The ferritic stainless steel type 430 stabilized with Nb, with and without annealing after hot rolling, was cold rolled and subjected to isothermal annealing at temperatures 650, 700 and 750°C for times ranging between 10 to 86400 s. The recrystallization kinetics was evaluated by JMAK model through microhardness measurements and KAM and GOS parameters. The Avrami exponent data indicate the occurrence of an unidimensional grain growth due only to high angle boundaries migration, with values ranging between 0.9 and 1.2. The nucleation rate and grain growth decreased continuously with time. The evolution of the texture was analyzed via EBSD analysis by ODF maps. The steel recrystallization is based on combination of ON and SG theories, due to presence of {111}<121>, {554}<225> and {111}<112> related to γ fiber. The rotated cube component, feature of the hot rolled steel, decreased with annealing time.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.