Abstract
The role of recrystallisation on structure–property relationship in Al-added medium-Mn steel was investigated at different stages of thermo-mechanical processing comprising of hot forging (HF), hot rolling (HR), cold rolling (CR) and intermediate annealing. The CR-annealed specimens have exhibited faster recrystallisation kinetics than HF-annealed and HR-annealed conditions, as reflected by the higher Avrami exponent (∼1.28) and requirement of minimum annealing temperature-time (1073K-50 min) for complete recrystallisation. The specimen cold rolled and annealed at 1073 K for 3 min (CR-1073K-3 min annealed) has exhibited excellent tensile properties owing to the co-existence of deformed and recrystallised grains. Further, the refinement of ferrite grains, lower austenite aspect ratio and higher volume fraction of γ-fibre of ferrite phase are responsible for better strength–ductility combination in the CR-1073K-3 min annealed specimen.This paper is part of a Thematic Issue on Medium Manganese Steels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.