Abstract
This study was conducted to recover silica (desilication) as a valuable metalloid from waste foundry sand (WFS) by a leaching process and to find application for desilicated foundry sand (DFS). The leaching time applied was 5 h; 3 M of potassium hydroxide (KOH) was used as a leaching reagent. The agitation speed of 200 rpm and the liquid/solid ratio of 25 were found to be the best conditions for optimum leaching results. A geopolymer from DFS was developed by using NaOH as an alkaline activator. The results obtained showed that the optimum conditions for the synthesis of a geopolymer were 15 M NaOH, 150 µm DFS particle size, and a curing temperature of 80 ℃ for 72 h. The geopolymer strength development was due to the formation of Phillipsite and Kalsilite as new hydration products. At the optimum alkaline solution concentration, the highest unconfined compressive strength (UCS) of 4.8 MPa was achieved. The developed geopolymer met the minimum strength requirements for load bearing material. This study provides an innovative and novel solution for the beneficiation of spent foundry sand and the recovery of a valuable metalloid, resulting to zero waste generation.Graphical
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.