Abstract
Dry shot blast generated during stainless steel production contains high content of valued metals such as iron chromium and nickel. These metals are in the form of oxides and it can be used as a raw material in iron and steel. This work aims to study the feasibility of metals recovery from dry shot blast by smelting reduction process. Smelting reduction of dry shot blast by using coking coal as reductant was conducted in an induction furnace. The effect of metallurgical parameters e.g. stoichiometry ratio of reductant per oxygen containing in dry shot blast, CaO/SiO2 of slag forming and CaF2 in slag, on %recovery of metal product was investigated. The results based on this study showed that the weight of metal product increases with increased the amount of coke to about 1.5 of stoichiometric molar ratio. Increasing of coke above this amount leads to decrease %recovery of metal product. Moreover, the weight of metal product is increased when the ratio of CaO/SiO2 in slag decreased from 2 to 1. The chemical composition of the metal product is in the range of commercial grade and it can be used as raw materials to produce steel and cast iron alloy.Dry shot blast generated during stainless steel production contains high content of valued metals such as iron chromium and nickel. These metals are in the form of oxides and it can be used as a raw material in iron and steel. This work aims to study the feasibility of metals recovery from dry shot blast by smelting reduction process. Smelting reduction of dry shot blast by using coking coal as reductant was conducted in an induction furnace. The effect of metallurgical parameters e.g. stoichiometry ratio of reductant per oxygen containing in dry shot blast, CaO/SiO2 of slag forming and CaF2 in slag, on %recovery of metal product was investigated. The results based on this study showed that the weight of metal product increases with increased the amount of coke to about 1.5 of stoichiometric molar ratio. Increasing of coke above this amount leads to decrease %recovery of metal product. Moreover, the weight of metal product is increased when the ratio of CaO/SiO2 in slag decreased from 2 to 1. The chemical composition of the metal product is in the range of commercial grade and it can be used as raw materials to produce steel and cast iron alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.