Abstract
AbstractSingle crystal tin selenide (SnSe) has a recorded high thermoelectric figure of merit (ZT) value of 2.6 at 923 K, but it is easy to form mechanical cracks and difficult to apply in thermoelectric conversion devices. Polycrystalline SnSe has better mechanical properties but inferior ZT values, which needs further optimization for applications. This work aims at enhancing the thermoelectric performance of polycrystalline SnSe through synergistic optimization of sliver (Ag) and aluminum (Al) co‐doping with the hydrogen reduction. The effects of Ag and Al doping on electronic transport properties are systematically investigated by density functional theory calculation and experimental measurement. Compared with pristine SnSe, Ag doping can effectively increase the hole concentration to 1.58 × 1019 cm−3 and improve the conductivity. Results also indicate that using Al dopant may slightly decrease the hole concentration but reduce the thermal excitation temperature, and introduce point defects reducing the lattice thermal conductivity through scattering phonons. In addition, the hydrogen reduction of sample powders before synthesis can effectively remove Sn oxides and reduce lattice thermal conductivity. At last, a state‐of‐the‐art maximum ZT value of 1.69 at 823 K is obtained in Ag0.01Al0.01Sn0.98Se. This study provides a theoretical basis and technical guidance for designing high‐performance polycrystalline SnSe.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.