Abstract
Extremely low reflectance was obtained from InP porous nanostructures in UV, visible, and near-infrared ranges. Porous samples were electrochemically prepared on which 130-nm-diameter nanopores were formed in a straight, vertical direction and were laterally separated by 50-nm-thick InP nanowalls. The reflectance strongly depended on the surface morphology. The lowest reflectance of 0.1% in the visible light range was obtained after the irregular top layer had been completely removed. Superior photoelectrochemical properties were obtained on the InP porous structures due to two unique features: the large surface area inside pores, and the large photon absorption enhanced on the low reflectance surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.