Abstract
Ammonium hydrogen carbonate was used as the precipitant to synthesize yttrium aluminate garnet (YAG) precursors from a mixed solution of aluminum and yttrium nitrates via coprecipitation. The carbonate precursor, with an approximate composition of NH4AlY0.6(CO3)1.9(OH)2 · 0.8H2O, transformed to pure YAG at 900 °C without the formation of intermediate phases. Reactive YAG powder was produced by calcining the precursor at 1100 °C. The YAG powder densified to 99.8% of the theoretical density by vacuum sintering at 1500 °C for 2 h, and the sintered body showed transparency. Less agglomeration of the precursor and good dispersity of the resultant YAG powder were responsible for the excellent sinterability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.