Abstract
The isotherm wetting and spreading behaviors of polycrystalline TiC by molten Zr55Cu30Al10Ni5 alloy were investigated at 1133 to 1253 K in a vacuum by using a modified sessile drop method. The system displays good wettability with the initial and final stable contact angles of 44 to 50° and 10 to 14°, respectively, mildly depending on the temperature. The spreading kinetics follows well defined exponential functions and could be described by a molecular dynamic model. On the other hand, a ZrC reaction layer was formed at the interface. The wetting was primarily promoted by the Zr adsorption at the triple junction and then by the formation of the reaction layer.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.